Study of Mechanical Properties of Hybrid Natural Fiber Composite

The present experimental study aims at learning the mechanical behaviour of hybrid natural fiber composites. Samples of several Jute-Bagasse-Epoxy & Jute-Lantana camara-Epoxy hybrids were manufactured using hand layup method where the stacking of plies was alternate and the weight fraction of fibre and matrix was kept at 40%-60%.Specimens were cut from the fabricated laminate according to the ASTM standards for different experiments. For Tensile test & flexural test samples were cut in Dog-bone shape and flat bar shape respectively. After that experiment is performed under Universal testing machine (UTM). ILSS (flexural strength) & Tensile strength were observed and compared to base values of epoxy polymer to perceive the change in strength. SEM analysis was done to ascertain the mode of failure