Preparation of Cu-based bulk metallic glasses by suction casting

A series of Cu-Hf-Ti alloys prepared by rapid solidification of the melt and by copper mould casting were studied in the present work. Alloy ingots were prepared by arc-melting mixtures of pure metals in an argon atmosphere. An indication of the cooling rate obtained was determined using an Al-4.5 wt%Cu alloy. Cooling rates varied from 540 K/s for the centre section of a 4 mm die to 885 K/s for the outside wall section of the 2 mm die. The glass-forming ability, structure and thermal stability of Cu-Hf-Ti glassy alloys were studied by X-ray diffraction (XRD), differential scanning calorimetry (DSC) and differential thermal analysis (DTA). Bulk glass formation was observed for the Cu64Hf36, Cu55Hf25Ti20 and Cu56Hf25Ti19 alloys, with critical diameters dc for a fully glassy structure of 1, 4 and 5 mm, respectively. The substitution of Hf by Ti increased the glassforming ability (GFA) and the thermal stability