Mobility-enhanced thermoelectric performance in textured nanograin Bi2Se3, effect on scattering and surface-like transport

Bayesteh S, Sailler S, Schloerb H, et al. Mobility-enhanced thermoelectric performance in textured nanograin Bi2Se3, effect on scattering and surface-like transport. Materials Today Physics . 2022;24: 100669.We report on the effect of artificially generated textures of Bi2Se3 in thermoelectric performance and low-temperature magnetoresistance. A set of texturized nanograined Bi(2)Se(3 & nbsp;)samples was investigated, ranging from predominantly c-axis texture to random texture. c-axis oriented layered domains rendered the samples highly conducting due to drastically enhanced mobility, up to 1600 cm(2)V-(1)s(-1) at low temperature, and enhanced both carrier concentration and electrical conductivity. The largest power factor of 800 mWm(-1)K(-2) and highest zT z 0.14 both at 300K were observed in a sample with a pre-dominantly layered and c-axis oriented texture. The random texture reduced the thermal conductivity, while the Seebeck coefficient showed no particular correlation with the texture. We have shown that the milling procedure generated a higher degree of disorder by increasing the milling frequency. As a result, the carrier scattering mechanism in the samples changed from mostly electron-phonon interaction at 5Hz to disorder-related scattering at 10Hz and 20Hz milling frequency. The weak antilocalization effect was observed in the magnetoresistance of pressed samples with different textures, pointing towards surface-like transport channels. The Hikami-Larkin-Nagaoka (HLN) model was used to evaluate the phase coherence length, resulting in a high value of roughly 600 nm regardless of the texture. However, a larger number of surface-like transport channels was obtained for the samples with random texture. (C)& nbsp;2022 Published by Elsevier Ltd