Impact of Tufa Stone Powder as a Partial Replacement of Aggregate on the Mechanical Performance and Durability of Repair Mortar

The rehabilitation and reconstruction works are usually performed with a view to conserving these landmarks and maintaining them culturally, architecturally and structurally. From this perspective, the mortars utilized in these repairs must be suitable, physiochemically and mechanically, to the ancient materials used in these buildings. Accordingly, it was proposed to evaluate tufa stone powder, a waste product of one of the most widely found stones in the Loire Valley in France, as an ingredient in repair-work mortar mixtures (M1, M2) through partially replacing the fine aggregate it contains with different amounts of this powder (37%, 42%) by weight of mix. Additionally, a third manufacturing mortar (M3) was utilized with both prepared mortars (M1, M2) for comparison with the tufa stone. The mechanical properties (including flexural, compressive and shear strengths, and ultrasonic pulse velocity) and the durability properties (total porosity, thermal dilation and conductivity, capillary absorption, and water and gas permeability) of the three mortars were examined in addition to those of the tufa stone. The results revealed that the prepared mortar, M2, (having lower binder content and a higher amount of substitution with tufa stone powder) has the lowest mechanical performance in comparison with the other mortars, indicating that this mortar is more supple and loose than the authentic tufa masonry. The thermal and durability properties are comparable to that of the tufa stone existent in ancient monuments. Consequently, the prepared mortar (M2) is the most appropriate mortar, for utilization in repairing old landmarks in the Loire Valley in France