Microencapsulation of active ingredients with polymers

Mikrokapsuliranje je metoda koja se često koristi u raznim granama industrije zbog široke mogućnosti upotrebe, a jedna od brojnih prednosti je što je moguće postići kontrolirano oslobađanje djelatne tvari. Cilj ovog istraživanja bio je proučiti i pripremiti mikrokapsule sušenjem raspršivanjem, mijenjajući procesne uvjete te udjele komponenti koje čine dozirni oblik; poli(vinil-alkohola) i dronedaron-hidroklorida. Pripremani su dozirni oblici poli(vinil-alkohola) i dronedaron-hidroklorida u masenim omjerima 1:1, 2:1 i 3:1, a otopine su sušene u laboratorijskom sušioniku Büchi B-290 pri četiri protoka zraka za raspršivanje. Morfologija dobivenih mikrokapsula ispitana je pomoću pretražnog elektronskog mikroskopa (SEM). Kinetika oslobađanja djelatne tvari iz mikrokapsula ispitana je in vitro laboratorijskim ispitivanjima, a dobiveni profili oslobađanja opisani su pomoću Weibullovog modela. Rezultati su pokazali da povećanjem protoka zraka za raspršivanje nastaju sitnije mikrokapsule što je potvrđeno i SEM-mikrografijama. Također, povećanjem udjela polimera veličina kapljica pod kontrolom je viskoznosti otopine, a ne protoka zraka za raspršivanje. Djelotvornost mikrokapsuliranja kod svih je dobivenih uzoraka veća od 50 %. Najujednačenija djelotvornost primijećena je kod uzoraka s omjerom polimera i djelatne tvari u odnosu 3:1. Mikrokapsule s najvećim udjelom polimera pokazale su najsporije oslobađanje djelatne tvari, a potpuno oslobađanje postignuto je nakon 24 sata.Microencapsulation is a method often used in various industries because of its wide use, and one of the many advantages is that controlled release of the active substance is achievable. The aim of this study was to study and prepare microcapsules by spray drying, changing the process conditions and proportions of the components that make up the dosage form; poly (vinyl alcohol) and dronedarone hydrochloride. Dosage forms of poly (vinyl alcohol) and dronedarone hydrochloride were prepared in 1: 1, 2: 1 and 3: 1 weight ratios, and the solutions were dried in a Büchi B-290 laboratory dryer at four spray air flows. The morphology of the obtained microcapsules was examined using a scanning electron microscope (SEM). The release kinetics of the active substance from the microcapsules were tested by in vitro laboratory testing and the resulting release profiles were described using the Weibull model. The results showed that by increasing the flow of spray air, smaller microcapsules are formed, as confirmed by SEM micrographs. Also, by increasing the polymer content, the droplet size is controlled by the viscosity of the solution, not by the flow of spray air. The microencapsulation efficiency of all samples obtained is greater than 50%. The most uniform efficacy was observed for samples with a 3: 1 ratio of polymer and active substance. Microcapsules with the highest polymer content showed the slowest release of the active substance, and complete release was achieved after 24 hours