Fatigue Damage Monitoring of CFRP Elements by Thermographic Procedure under Bending Loads

Abstract: For structural health of mechanical structures, non-destructive detection and material defect characterization represent the main useful tools for mechanical decay prediction caused by local composite damage phenomena. In this work, internal delamination due to alternate bending were characterized in flat specimens, performing fatigue and static tests, coupled with thermographic, optical, and ultrasonic analysis for damage detection and evolution purposes. Damage to rupture behavior of CFRP material through mechanical tensile tests is performed on several samples and non-destructive inspection procedures are optimized during successive HCF tests to detect in real time local compliance variations and damage initiation. Thermographic continuous monitoring and occasional ultrasonic analysis are implemented to analyze composite anomalies during fatigue life and to elaborate a procedure for identification of delamination induced damage before failure. IRT and UT results are computed with MATLAB analysis for damage evaluation with strain and compliance data acquired during tests