Synthesis and characterisation of porous, calcium enriched coatings formed on Titanium via Plasma Electrolytic Oxidation

The SEM and EDS study results of porous and calcium enriched coatings obtained via Plasma Electrolytic Oxidation (Micro Arc Oxidation) on the Commercial Purity Titanium Grade 2 samples, at three potentials 450 VDC, 550 VDC, 650 VDC in electrolytes containing 500 g Ca(NO3)2∙4H2O in 1000 mL H3PO4, are presented in the paper. In the same electrolyte three Titanium samples, one after other, were treated, with the PEO processing time equaling 3 minutes after each immersion. Based on SEM and EDS results, it was possible to state that all obtained coatings are porous and their calcium-to-phosphorus (Ca/P) ratio decreases with decreasing PEO voltage. In addition, it was found out that electrolyte aging results in decreasing Ca/P ratio, too