Wpływ struktury chemicznej biopolioli z oleju rzepakowego na wybrane właściwości pianek poliuretanowych

In this work, we report on obtaining rigid polyurethane foams with biopolyols based on rapeseed oil. The biopolyols with different functionality were synthesized in a two-stage reaction of oil epoxidation and oxirane ring opening with 1-hexanol (P_1Hex) and 1,6-hexanediol (P_1.6Hex) and their properties were characterized (Table 2, Figs. 1–3). Next, they were used to replace petrochemical polyols in foams by up to 60% by mass (Table 1). The introduction of the biopolyols into the polyurethane systems affected their reactivity (Fig. 4). The replacement of the petrochemical polyols with the biopolyols caused changes in the cell structure (Tables 3, 4) and the physical and mechanical properties of the resultant materials (Table 5).Sztywne pianki poliuretanowe otrzymano z udziałem biopolioli z oleju rzepakowego. Biopoliole o różnej funkcyjności zsyntetyzowano w dwuetapowej reakcji epoksydacji oleju i otwarcia pierścieni oksiranowych za pomocą 1-heksanolu (P_1Hex) i 1,6-heksanodiolu (P_1.6Hex), a następnie je scharakteryzowano (tabela 2, rys. 1–3). Piankę referencyjną modyfikowano w wyniku zastąpienia poliolu petrochemicznego biopoliolami w ilości do 60% mas. (tabela 1). Wprowadzenie biopolioli do systemów poliuretanowych wpłynęło na zmniejszenie ich reaktywności (rys. 4). Zastąpienie poliolu petrochemicznego biopoliolami spowodowało zmiany struktury komórkowej (tabele 3 i 4) i właściwości fizyko-mechanicznych otrzymanych materiałów (tabela 5)