Stopy Pt-Rh: badanie wytrzymałości na rozciąganie i wydłużenia w wysokich temperaturach

In this paper are presented investigation results of tensile strength and elongation of selected alloys from Pt-Rh system. Samples with the content of rhodium in a concentration range of 7-40% (wt.) were studied. Studies were performed in the temperature range 1100-1500°C at a stress of 2-20 MPa. A universal device for measuring hardness was used to measure the Vickers hardness. For investigation of time strength and elongation at high temperatures, the device Mayes MK2 TC/10 was used. It was found that the value of tensile strength increases with increasing rhodium content, and decreases with increasing temperature. Elongation decreases to 7% Rh, then increases with increasing rhodium content to 15% and then slowly decreases again. With increasing temperature there is a slight increase in elongation.W pracy przedstawiono wyniki badań wytrzymałości na rozciąganie i wydłużenia wybranych stopów z układu Rh-Pt. Zbadane zostały próbki z zawartości rodu w zakresie 7-40% wag. Pomiar twardości Vickersa przeprowadzono w zakresie temperatur 1100-1500°C, przy naprężeniu 2-20 MPa, przy użyciu uniwersalnego urządzenia do pomiaru twardości. Do badania wytrzymałościna rozciąganie i wydłużenia w wysokich temperaturach zastosowano urządzenie Mayes MK2TC/10. Stwierdzono, że wytrzymałość na rozciąganie zwiększa się wraz ze wzrostem zawartości rodu i zmniejsza się wraz ze wzrostem temperatury. Wydłużenie zwiększa się wraz ze wzrostem zawartości rodu od 7% do 15%, a następnie powoli zmniejsza się ponownie w zakresie od 15% do 40% rodu. Wraz ze wzrostem temperatury obserwowany jest niewielki wzrost wydłużenia