Contribution of Microstructural Constituents on Hot Cracking of MAR-M247 Nickel Based Superalloy

The aim of this study is to investigate influence of selected parameters of gas tungsten arc welding on microstructure of MAR-M247 nickel based superalloy originating from turbine vane. MAR-M247 is a precipitation-strengthened superalloy which is widely used in aerospace engines. The main strengthening phase in this material is ordered L12 intermetallic γ' phase Ni3 (Al, Ti). The surface of alloy was modified by electric arc in order to present microstructural changes in weld and heat affected zone. Investigation of the heat affected zone revealed that constitutional liquation of γ' particles and primary carbides is responsible for the formation of a liquid grain boundary layer which finally contributed to cracking. Scanning electron microscopy indicated high susceptibility to cracking of MAR-M247 alloy which is connected with high content of γ'-formers aluminum and titanium