Wpływ temperatury odpuszczania na twardość i udarność stali 56NiCrMo7

The assessment of the effect of tempering temperature on hardness and impact toughness of a 56NiCrMo7 grade hot work tool steel was presented in the paper. It has been found that the investigated steel, after quenching in oil from 800°C, softens quite slowly upon tempering within the range between 100 and 675°C, which was confirmed not only by hardness measurements but also by observed changes occurring in its microstructure, whereas the impact energy (KV) absorbed by the test specimen increases with temperature, achieving >66J after tempering at 675°C. The changes observed in the character of the fracture surfaces allows of interpretation of the impact test results for the whole range of tempering temperatures.W artykule przedstawiono wyniki badań na temat wpływu temperatury odpuszczania na twardość i udarność stali narzędziowej do pracy na gorąco w gatunku 56NiCrMo7. Badania wykonano dla wybranej temperatury austenityzowania równej 800°C. Wykazano, że badana stal zahartowana w oleju od tej temperatury a następnie odpuszczona w zakresie 100-675°C mięknie dość wolno, co potwierdziły nie tylko wyniki pomiarów twardości ale również obserwacje zmian zachodzących w jej mikrostrukturze. Praca złamania (KV) próbki udarnościowej rośnie ze wzrostem temperatury odpuszczania, przekraczając 66 J po odpuszczaniu w 675°C. Potwierdzeniem uzyskanych wyników badan udarności są zmiany zaobserwowane w charakterze przełomów próbek w całym zakresie temperatur odpuszczania