Wpływ katodowej gęstości prądu na mikrostrukturę i właściwości niklowych powłok kompozytowych

Studies were carried out to characterise the nickel composite coatings deposited on a 2xxx series aluminium alloy. The composite coatings were prepared in a Watts bath with the addition of fine-dispersed particles of Al2O3 powder introduced in an amount of 100 g/l using current densities of 2, 4, 6 and 8 A/dm2. The morphology, structure, thickness and microhardness of the obtained composite coatings were described. The volume fraction of Al2O3 particles in composite coating was determined. The corrosion resistance of thus produced coatings was examined. Based on the results of the conducted studies it was stated that all the produced coatings were characterised by good adhesion to the substrate, but coatings produced at high current densities were characterised by a lower content of the Al2O3 reinforcing phase present in the composite.W pracy przedstawiono badania charakteryzujące kompozytowe powłoki niklowe osadzane na stopie aluminium serii 2xxx. Powłoki kompozytowe wytwarzano w kąpieli Wattsa z dodatkiem drobnodyspersyjnych cząstek proszku AI2O3 w ilości 100 g/l przy zastosowaniu gęstości prądu: 2, 4. 6 oraz 8 A/dm2. Przedstawiono morfologię, strukturę, grubość oraz mikrotwardość uzyskanych powłok kompozytowych. Określono objętościowy udział cząstek AI2O3 w powłoce kompozytowej. Zbadano odporność korozyjną wytworzonych powłok. Na podstawie przeprowadzonych badań stwierdzono, iż wszystkie uzyskane powłoki są dobrze przyczepne do podłoża, jednak powłoki uzyskane przy wyższych gęstościach prądów charakteryzują się niższą zawartością fazy zbrojącej AI2O3 w kompozycie