Charakterystyka procesu kształtowania warstw stopowych na odlewach staliwnych

A description of alloy layer formation on a steel substrate is presented. Two types of formation are considered: diffusion of carbon and chromium into the solid from the pad in the direction of the cast steel within the FeCrC (grains) and diffusion in a layer of liquid chromium cast iron formed in a preceding step. The influence of silicon in the pad on the pad’s transformation into the liquid is also examined. Solidus and liquidus temperatures of high carbon ferrochromium are determined. The larger the content of Si is used in the experiment, the lower the solidus temperature of the FeCrC alloy is observed. This results from the higher intensity of the elements’ diffusion and faster formation of the liquid.W pracy przedstawiono autorski opis procesu powstawania powierzchniowej warstwy stopowej, którego istota opiera się na dyfuzji w stanie stałym węgla i chromu z wkładki w stronę staliwa w obrębie ziaren FeCrC, jak również na dyfuzji w warstwie ciekłego żeliwa chromowego powstałego w wcześniejszych etapach tworzenia się warstwy w wyniku dyfuzji w stanie stałym. Zbadano również wpływ dodatku krzemu w materiale wkładki stopowej na proces przejścia jej w stan ciekły. Określono temperaturę likwidus i solidus żelazochromu wysokowęglowego mającą wpływ na ten proces. Stwierdzono, że zwiększona zawartość Si powoduje obniżenie temperatury solidus stopu FeCrC co jest powodem zwiększenia szybkości dyfundujących składników, co z kolei prowadzi do szybszego powstania fazy ciekłej