Właściwości użytkowe przerabianego plastycznie stopu magnezu ZK60A

The object of this study was to develop parameters of plastic deformation process of magnesium alloy - ZK60A. The tests have showed that for this alloy it is possible to use the temperature of the plastic deformation process ranging from 350°C to 450°C. Samples were characterized by mechanical properties and structure in different heat treatment tempers. This magnesium alloy obtained in the T5 temper higher mechanical properties then T6 temper. The paper also presents research results of investigation of conversion coating on ZK60A magnesium alloy by anodic oxidation method in non-chromium solutions. It was found that the coating produced in non-chromium solutions show considerable increase of corrosion resistance of tested alloy.Przedmiotem prezentowanej pracy było określenie możliwości kształtowania plastycznego na gorąco półwyrobów ze stopu magnezu ZK60A. Z przeprowadzonych prób wynika, iż dla tego stopu można stosować temperaturę przeróbki plastycznej materiału z zakresu 350°C÷50°C. Otrzymane półwyroby scharakteryzowano pod kątem właściwości mechaniczne i struktury w różnych stanach umocnienia wydzieleniowego. Stop ten uzyskuje wyższe właściwości mechaniczne w stanie T5 niż dla stanu T6. W pracy przedstawiono wyniki badań dotyczące wytwarzania powłok konwersyjnych na stopie magnezu ZK60A metodą utleniania anodowego w roztworach bezchromianowych. Stwierdzono, że wytworzone powłoki w roztworach bezchromianowych powodują wrzrost odporności na korozję badanego stopu