Wpływ stopniowego hartowania izotermicznego na skład fazowy oraz właściwości mechaniczne stali X37CrMoV5-1 o strukturze nanokrystalicznej

This paper presents the results of studies of X37CrMoV5-1 steel subjected to quenching processes with a one-step and a two-step isothermal annealing. The TEM observation revealed that steel after one-step treatment led is composed of carbide-free bainite with nanometric thickness of ferrite plates and of high volume fraction of retained austenite in form of thin layers or large blocks. In order to improve the strength parameters an attempt was made to reduce the austenite content by use of quenching with the two-step isothermal annealing. The temperature and time of each step were designed on the basis of dilatometric measurements. It was shown, that the two-step heat treatment led to increase of the bainitic ferrite content and resulted in improvement of steel's strength with no loss of steel ductility.W artykule przedstawiono wyniki badań stali X37CrMoV5-1 poddanej hartowaniu izotermicznemu jedno i dwu stopniowemu. Obserwacji TEM wykazały, że stal po jednostopniowym hartowaniu izotermicznym składa się z bainitu bezwęglikowego o nanometrycznej grubości płytek ferrytu poprzedzielanych cienkimi warstwami lub blokami austenitu. Wysoka plastyczność stali wynika z wysokiej zawartością fazy austenitycznej. W celu poprawy parametrów wytrzymałościowych postanowiono zmniejszyć ilość austenitu poprzez zastosowanie dwustopniowego hartowania izotermicznego. Parametry tego procesu zostały zaprojektowane na podstawie badań dylatometrycznych. Wykazano, że dwustopniowa obróbka cieplna prowadził do podwyższenia zawartości ferrytu bainitycznego i tym samym do poprawy wytrzymałości stali bez utraty plastyczności