Otrzymywanie PZT domieszkowanego Mn do kompozytów ceramiczno-polimerowych

Lead zirconate titanate (PZT) ceramics, with general chemical formula Pb(Zr1-xTix)O3 are used in numerous piezo- and pyroelectric applications. In practice, PZT is rarely used in a chemical pure form. The dielectric, piezoelectric and pyroelectric properties of PZT can be modified by adding dopants to the ABO3-type PZT perovskite structure. Ceramics powders of manganese-doped lead zirconate titanate with composition Pb(Zr0.3Ti0.7)0.97Mn0.03O3 (PMZT) were prepared by the sol-gel method using: lead(II)acetate trihydrate, zirconium(IV)propoxide, titanium(IV)propoxide and manganese(II)acetate tetrahydrate as precursors. The PMZT-PVC composites were fabricated from PMZT and polymer powders by hot-pressing method.Ceramiczne roztwory stałe cyrkonianu tytanianu ołowiu (PZT) o wzorze ogólnym Pb(Zr1-xTix)O3 znajdują szerokie zastosowanie jako piezo- i piroelektryki. W praktyce czysty PZT jest rzadko używany. Właściwości piezoelektryczne i piroelektryczne PZT modyfikuje się poprzez dodawanie domieszek do struktury typu perowskitu ABO3. Ceramiczne proszki cyrkonianu tytanianu ołowiu domieszkowanego manganem o składzie Pb(Zr0;3Ti0;7)0;97Mn0;03O3 (PMZT) otrzymano metodą zolowo-żelową. Jako prekursorów użyto: octanu ołowiu, propanolanu cyrkonu, propanolanu tytanu i octanu manganu. Kompozyty ceramiczno-polimerowe PMZT-PVC otrzymano z proszku PMZT i proszku polimeru PVC metoda prasowania na gorąco