The Influence of the Angle of Working Part of Die on the Zinc Coating Thickness and Mechanical Properties of Medium Carbon Steel Wires

The paper discusses experimental studies to determine the effect of the die working portion angle on the lubrication conditions, zinc coating thickness and the mechanical properties of medium-carbon steel wires. The test material was 5.5 mm-diameter wire rod which was drawn into 2.2 mm-diameter wire in seven draws at a drawing speed of v = 10 m/s. Conventional drawing dies of a working portion angle of α = 3, 4, 5, 6, 7°, respectively, were used for the drawing process. After the drawing process, the quantity of the lubricant on the wire surface and the thickness of the zinc coating were determined in individual draws. Testing the finished 2.2 mm-diameter wires for mechanical properties, on the other hand, determined the effect of the die working portion on the yield point, tensile strength, uniform and total elongation, reduction in area, the number of twists and the number of bends