Wpływ osadzania nanostrukturalnych powłok na odporność kawitacyjną stali austenitycznej X6CrNiTi18-10

The results of the cavitation erosion resistance of nanostructure TiN, CrN and WC/a:C-H coatings deposited on X6CrNiTi18-10 stainless steel by means of PVD method are shown. The tests of cavitation resistance were performed in a cavitation tunnel with a barricade system. It was noticed that the deposition of TiN and CrN nanocrystalline coatings has improved the cavitation resistance of X6CrNiTi18-10 stainless steel while the deposition of WC/a:C-H nanocomposite coating has decreased the cavitation resistance. The high adhesion and good plastic deformation abilities of coatings are very important to assure the high cavitation resistance of the austenitic steel-hard coating system.W pracy przedstawiono wyniki badań kawitacyjnych powłok TiN, CrN oraz WC/a:C-H osadzonych metodą PVD na stali X6CrNiTi18-10. Uzyskano, że nanokrystaliczne powłoki TiN oraz CrN poprawiły odporność kawitacyjną, natomiast nanokompozytowa powłoka WC/a:C-H spowodowała pogorszenie odporności kawitacyjnej. Przeprowadzone badania wykazały, iż wysoka adhezja i dobre własności plastyczne są istotnymi własnościami powłok, przeznaczonymi dla ochrony materiałów przed erozją kawitacyjną