Mechanism and Timescales of Reversible p Doping of Methylammonium Lead Triiodide by Oxygen

Understanding and controlling the energy level alignment at interfaces with metal halide perovskites MHPs is essential for realizing the full potential of these materials for use in optoelectronic devices. To date, however, the basic electronic properties of MHPs are still under debate. Particularly, reported Fermi level positions in the energy gap vary from indicating strong n to strong p type character for nominally identical materials, raising serious questions about intrinsic and extrinsic defects as dopants. In this work, photoemission experiments demonstrate that thin films of the prototypical methylammonium lead triiodide MAPbI3 behave like an intrinsic semiconductor in the absence of oxygen. Oxygen is then shown to be able to reversibly diffuse into and out of the MAPbI3 bulk, requiring rather long saturation timescales of almost equal to 1 h in ambient air and over 10 h out ultrahigh vacuum , for few 100 nm thick films. Oxygen in the bulk leads to pronounced p doping, positioning the Fermi level universally almost equal to 0.55 eV above the valence band maximum. The key doping mechanism is suggested to be molecular oxygen substitution of iodine vacancies, supported by density functional theory calculations. This insight rationalizes previous and future electronic property studies of MHPs and calls for meticulous oxygen exposure protocol