Comportement thermomécanique d'un composite de type SiC/SiC

In SiC/PyC/SiC composites, initially developed for high-temperature structural applications, the pyrocarbon interface is sensitive to oxidation. The addition of boron in the matrix promotes the formation of a glass that allows the healing of cracks. The thermomechanical behavior of this SiC/SiBC material has therefore been studied at temperatures between 700c and 1200c, under inert or oxidizing atmosphere in uniaxial traction, static or cyclic fatigue. This work made it possible to determine the contribution of residual stresses on matrix cracking, the influence of the initial state of damage of the matrix on the creep rate and finally the mechanisms of behavior and hot rupture under air that depend on the speed of installation of the glass protection and its tightness.Dans les composites SiC/PyC/SiC, initialement développés pour des applications structurales à hautes températures, l'interface de pyrocarbone est sensible à l'oxydation. L'addition de bore dans la matrice favorise la formation d'un verre qui permet la cicatrisation des fissures. Le comportement thermomécanique de ce matériau SiC/SiBC a donc été étudié à des températures comprises entre 700c et 1200c, sous atmosphère inerte ou oxydante en traction uniaxiale, en fatigue statique ou cyclique. Ce travail a permis de déterminer la contribution des contraintes résiduelles sur la fissuration matricielle, l'influence de l'état d'endommagement initial de la matrice sur la vitesse de fluage et enfin les mécanismes de comportement et de rupture à chaud sous air qui dépendent de la vitesse de mise en place de la protection vitreuse et de son étanchéité