Local approach of fracture on semi-crystalline polymers : contribution of X-ray laminography technique

International audienceDamage mechanisms in a PolyAmide 6 semi-crystalline polymer were characterized by using Synchrotron Radiation Laminography technique on CT like specimen. Damage appeared as multiple penny shaped crazes. The maximum damage occurred at mid-thickness and located at a small distance from the notch root. An attempt was made to apply local approach of fracture concept thanks to finite element analysis using damage-based constitutive model. FE simulation successfully captured the aforementioned micro-mechanisms of crack initiation, by void coalescence. Further work is carried out to determine the crack dimension corresponding to the maximum net stress: the criterion being used for the global approach of fracture