The Effect of Ceramic Restoration Shade and Thickness on the Polymerization of Light and Dual-cure Resin Cements

OBJECTIVES: Inadequately polymerized resin cements may negatively affect the clinical performance of cemented all-ceramic restorations. The purpose of this in vitro study was to evaluate the effect of ceramic thickness and shade on the microhardness of various light-cured (LC) and dual-cured (DC) resin cements. The amount of light transmission through the restoration was also evaluated to correlate the results. METHODS: Three different brands of resin cements (Appeal/Ivoclar; Calibra/Dentsply; Nexus 2/Kerr) were used in LC and DC forms to prepare disk-shaped samples (0.5-mm thickness × 5-mm diameter) (n=15). Study group samples were light-cured for 40 seconds (Flashlite 1401/Discus Dental) through four shades (ETC1, ETC2, ETC3, ETC4) and four thicknesses (1 mm, 2 mm, 3 mm, 4 mm) of all-ceramic ingot discs (IPS Empress Esthetic/Ivoclar). Control samples were directly cured without the presence of ceramic. The light transmission through various shades and thicknesses of ceramics was measured using a hand-held radiometer (Demetron, Kerr). Vickers microhardness measurements were performed (Micromet/Buehler) at 24 hours following dark storage in 37°C water. Correlation between ceramic shade, thickness, and light intensity readings (mW/cm2) with respect to microhardness was statistically evaluated using analysis of variance (p=0.05). RESULTS: Ceramic thickness of 3 mm and/or above significantly decreased the microhardness values in all LC and DC groups (p\u3c0.0001). Ceramic shade had a significant effect only on Calibra in both LC and DC groups (p\u3c0.0001). Microhardness values of LC groups were significantly lower than DC groups (p\u3c0.0001). Control groups had significantly higher hardness values in all cement groups (p\u3c0.0001). There was a significant correlation between the amount of light transmitted and hardness (p=0.000). CONCLUSION: The ceramic thickness has a more intense effect on polymerization compared to the ceramic shade. Overlying ceramic thickness of 3 mm and above was found to adversely affect the polymerization of LC and DC resin cements and therefore a 3-mm thickness was considered the critical threshold