Crack propagation in 3PB specimen has been investigated experimentally by using Digital Image Correlation (DIC) technique. For this purpose, specimens were taken from butt welded plates, made of P460NL1 micro-alloyed steel. Fatigue pre-crack of 3PB specimens was introduced in the weld metal. Specimens were then statically loaded and analyzed using digital image correlation software ARAMIS to assess strain fields and crack propagation paths. Bifurcation of cracks was noticed as the main characteristics of crack prop-agation in the analyzed case
The mechanical behaviour of heterogeneous regions like weldings is strongly affected by the local re...
AbstractRecent technological improvements in digital photography have made Digital Image Correlation...
In dynamical loaded welded structures fatigue life is often a limiting factor. Common practise is to...
Crack propagation in 3PB specimen has been investigated experimentally by using Digital Image Correl...
Fatigue crack growth in the Heat Affected Zone (HAZ) of a welded CrNiMoV steel has been investigated...
It is proposed to use digital image correlation (DIC) to identify parameters governing crack propaga...
The aim of this investigation was to identify sources of AE in mild steel fatigue specimens and rel1...
Digital image correlation (DIC) is more and more utilized in experimental mechanics. It is a contact...
The method based on the digital image correlation (DIC) technique and thermoelastic stress analysis ...
This thesis is concerned with the evaluation, in-situ, of the elastic strain energy release rate of ...
Acoustic emission (AE) is a passive form of non-destructive testing that relies on the detection of ...
The present paper exposes the development of a specific Digital Image Correlation (DIC) method to e...
The present paper investigates crack growth in specially designed specimens of 6061 aluminum alloy s...
For electronic devices, solder joint is a weakness that easily leads to failure during working. Ther...
The trajectory of fatigue crack growth is influenced by many parameters and can be irregular due to ...
The mechanical behaviour of heterogeneous regions like weldings is strongly affected by the local re...
AbstractRecent technological improvements in digital photography have made Digital Image Correlation...
In dynamical loaded welded structures fatigue life is often a limiting factor. Common practise is to...
Crack propagation in 3PB specimen has been investigated experimentally by using Digital Image Correl...
Fatigue crack growth in the Heat Affected Zone (HAZ) of a welded CrNiMoV steel has been investigated...
It is proposed to use digital image correlation (DIC) to identify parameters governing crack propaga...
The aim of this investigation was to identify sources of AE in mild steel fatigue specimens and rel1...
Digital image correlation (DIC) is more and more utilized in experimental mechanics. It is a contact...
The method based on the digital image correlation (DIC) technique and thermoelastic stress analysis ...
This thesis is concerned with the evaluation, in-situ, of the elastic strain energy release rate of ...
Acoustic emission (AE) is a passive form of non-destructive testing that relies on the detection of ...
The present paper exposes the development of a specific Digital Image Correlation (DIC) method to e...
The present paper investigates crack growth in specially designed specimens of 6061 aluminum alloy s...
For electronic devices, solder joint is a weakness that easily leads to failure during working. Ther...
The trajectory of fatigue crack growth is influenced by many parameters and can be irregular due to ...
The mechanical behaviour of heterogeneous regions like weldings is strongly affected by the local re...
AbstractRecent technological improvements in digital photography have made Digital Image Correlation...
In dynamical loaded welded structures fatigue life is often a limiting factor. Common practise is to...