Growth of centimeter-scale perovskite single-crystalline thin film via surface engineering

Modern electronic and photonic devices rely on single-crystalline thin film semiconductors for high performance and reproducibility. The emerging halide perovskites have extraordinary electronic and photonic properties and can be synthesized via low cost solution-based methods. They have been used in a variety of devices with performance approaching or over the devices based on conventional materials. However, their solution based growth method is intrinsically challenge to grow large scale single-crystalline thin film due to the random nucleation and isotropous growth of the crystal. Here, we report the growth of centimeter-scale perovskite single-crystalline thin films by controlling the nucleation density and growth rate of the crystal under a spatially confined growth condition. The hydrophobic treatment on substrates inhibits nucleation and accelerates the growth of single-crystalline thin film, providing enough space for initial nucleus growing up quickly without touching each other. Single-crystalline perovskite thin-film with an aspect ratio of 1000 (1 cm in side length, 10 mu m in thickness) has been successfully grown. The low trap density and the high mobility of the as-grown thin film show a high crystallinity. The photodetector based on the perovskite thin film has achieved a gain similar to 10(4), benefitting from the short transit time of the carries due to the high mobility and thin thickness of the active layer. Our work opens up a new route to grow large scale perovskite single-crystalline thin films, providing a platform to develop high- performance devices