HREM studies of the structure and the oxidation process of copper clusters created by inert gas aggregation

Structure and reactivity with oxigen of Cu clusters in the size range of 4.5±2.5 nm created by the inert gas aggregation technique were studied by HREM. The pure Cu clusters investigated under clean conditions show the structures of MTP's with a small lattice dilatation of the (111) plane of 1.25%. For icosahedral and decahedral particles this dilatation corresponds to a splitting of the nearest neighbour distance showing two different values, i.e. dilatation of 2.2% and contraction of 2.8% for the two edges of the deformed tetrahedral subunits, respectively. Oxidation at room temperature and air pressure of 1 bar only begins after a few minutes of exposure to air, after having undergone creation of probably non-stoichiometric intermediate states in the cuprite Cu2O structure with the bulk values of the bond lengths