Study on the Absorption Characteristics and Laser Damage Properties of Fused Silica Optics under Flexible Polishing and Shallow DCE Process

The enhancement of laser damage resistance of fused silica optics was a hotspot in scientific research. At present, a variety of modern processes have been produced to improve the laser induced damage threshold (LIDT) of fused silica optics. They included pre-treatment processes represented by flexible computer controlled optical surfacing (CCOS), magnetorheological finishing (MRF), ion beam finishing (IBF), and post-treatment processes represented by dynamic chemical etching (DCE). These have achieved remarkable results. However, there are still some problems that need to be solved urgently, such as excessive material removal, surface accuracy fluctuation in the DCE process, and the pollution in MRF process, etc. In view of above problems, an MRF, CCOS, IBF and shallow DCE combined technique was used to process fused silica optics. The surface morphology could be greatly controlled and chemical etching depth was reduced, while the LIDT increased steadily. After processing by this combined technique, the LIDT increased to 12.1 J/cm2 and the laser damage resistance properties of fused silica were significantly enhanced. In general, the MRF, IBF, CCOS and shallow DCE combined technique brought much help to the enhancement of laser damage resistance of fused silica, and could be used as a process route in the manufacturing process of fused silica