Laboratory Study of Deformational Characteristics and Acoustic Emission Properties of Coal with Different Strengths under Uniaxial Compression

Acoustic emission (AE) can reflect the dynamic changes in a material’s structure, and it has been widely used in studies regarding coal mechanics, such as those focusing on the influence of loading rate or water content change on the mechanical properties of coal. However, the deformational behavior of coals with various strengths differs due to the variation in microstructure. Hard coal presents brittleness, which is closely related to certain kinds of geological disasters such as coal bursts; soft coal exhibits soft rock properties and large deformation mechanical characteristics. Therefore, conclusions drawn from AE characteristics of a single coal sample have application limitations. This paper studies the deformation patterns and AE characteristics of coals with different strengths. A uniaxial compression experiment was carried out using coal samples with average uniaxial compressive strengths of 30 MPa and 10 MPa; the SAEU2S digital AE system was used to measure the AE counts, dissipation energy, and fracturing point distributions at each deformation stage of the different coals. The results show that the bearing capacity of hard coal is similar to that of the elastic stage and plastic deformation stage, but it may lose its bearing capacity immediately after failure. Soft coal has a relatively distinct stress-softening deformation stage and retains a certain bearing capacity after the peak. The AE counts and dissipation energy of hard coal are significantly higher than those of soft media, with average increases of 49% and 26%, respectively. Via comparative analysis of the distribution and development of internal rupture points within soft coal and hard coal at 15%, 70%, and 80% peak loads, it was observed that hard coal has fewer rupture points in the elastic deformation stage, allowing it to maintain good integrity; however, its rupture points increase rapidly under high stress. Soft coal produces more plastic deformation under low loading conditions, but the development of the fracture is relatively slow in the stress-softening stage. We extracted and summarized the AE characteristics discussed in the literature using one single coal sample, and the results support the conclusions presented in this paper. This study subdivided the deformation process and AE characteristics of soft and hard coals, providing a theoretical guidance and technical support for the application of AE technology in coal with different strengths