Sulfidation-Oxidation Resistance of Thermal Diffusion Multi-Layered Coatings on Steels

The high-temperature sulfidation-oxidation corrosion resistance of protective coatings deposited on carbon and 316L steels was studied. The coatings obtained via the thermal diffusion process had multi-layered architectures and consisted of aluminides, iron borides, or iron boride–TiO2 layers. The protective coatings experienced a minimal rate of mass changes, insignificant scale formation, and no delamination and surface micro-cracking after 504 h of exposure in 1% (Vol.) H2S-air atmosphere at 500 °C. Furthermore, the coatings demonstrated a high degree of integrity compared to bare 316L stainless steel. Aluminized steels demonstrated the highest performance among the studied materials. The developed thermal diffusion coatings are promising candidates due to their enhanced stability in H2S–air atmosphere; they may be employed for protection of inner and outer surfaces of long tubing and complex shape components