Unidirectional solidification of a Zn-rich Zn-2.17 wt%Cu hypo-peritectic alloy
- Ma, D.
- Li, Y.
- Ng, S.C.
- Jones, H.
DOIAbstract
10.1016/S1468-6996(01)00038-9Science and Technology of Advanced Materials21127-13
10.1016/S1468-6996(01)00038-9Science and Technology of Advanced Materials21127-13
In the present work, the effect of growth rate and temperature gradient on microstructure and mechan...
Directional solidification experiments on Cu-Sn peritectic alloys have been conducted at very low ve...
Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)Conselho Nacional de Desenvolvimento Ci...
WOS: 000271352200021Zn-0.7 wt% Cu-hypoperitectic alloy was prepared in a graphite crucible under a v...
Zn-1.5wt.%Cu peritectic alloy was prepared in a graphite crucible under a vacuum atmosphere. Unidire...
O desenvolvimento de microestruturas durante a solidificação de ligas peritéticas tem muito interess...
Transient directional solidification experiments have been carried out with Zn-Mg hypoeutectic alloy...
Zn-1.5wt.% Cu peritectic alloy was directionally solidified upward with different growth rates (8.41...
Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)Conselho Nacional de Desenvolvimento Ci...
Although Zn–Sn alloys have suitable features for high temperature solders, as for example the absenc...
In this work, the microstructural evolution of Zn–3.2 wt%Ag (hypoperitectic) and Zn–8 wt%Ag (hyperpe...
The most relevant range of compositions of Zn–Sn high-temperature solder alloys remains between 10 a...
AbstractIn the present research the horizontal directional solidification of Zn-Sn alloys (Zn-4wt.%S...
WOS: 000274947700006Zn-0.7wt.%Cu hypoperitectic alloys were directionally solidified upwards with di...
AbstractDirectional growth of Zn-Al alloys of different concentration was carried out by using a Bri...
In the present work, the effect of growth rate and temperature gradient on microstructure and mechan...
Directional solidification experiments on Cu-Sn peritectic alloys have been conducted at very low ve...
Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)Conselho Nacional de Desenvolvimento Ci...
WOS: 000271352200021Zn-0.7 wt% Cu-hypoperitectic alloy was prepared in a graphite crucible under a v...
Zn-1.5wt.%Cu peritectic alloy was prepared in a graphite crucible under a vacuum atmosphere. Unidire...
O desenvolvimento de microestruturas durante a solidificação de ligas peritéticas tem muito interess...
Transient directional solidification experiments have been carried out with Zn-Mg hypoeutectic alloy...
Zn-1.5wt.% Cu peritectic alloy was directionally solidified upward with different growth rates (8.41...
Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)Conselho Nacional de Desenvolvimento Ci...
Although Zn–Sn alloys have suitable features for high temperature solders, as for example the absenc...
In this work, the microstructural evolution of Zn–3.2 wt%Ag (hypoperitectic) and Zn–8 wt%Ag (hyperpe...
The most relevant range of compositions of Zn–Sn high-temperature solder alloys remains between 10 a...
AbstractIn the present research the horizontal directional solidification of Zn-Sn alloys (Zn-4wt.%S...
WOS: 000274947700006Zn-0.7wt.%Cu hypoperitectic alloys were directionally solidified upwards with di...
AbstractDirectional growth of Zn-Al alloys of different concentration was carried out by using a Bri...
In the present work, the effect of growth rate and temperature gradient on microstructure and mechan...
Directional solidification experiments on Cu-Sn peritectic alloys have been conducted at very low ve...
Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)Conselho Nacional de Desenvolvimento Ci...
Add to ORKG