Add to ORKGWe report the heat capacity and magnetic properties of single crystals of YbPd2Si2 grown from Sn flux. YbPd2Si2 is a non magnetic heavy fermion compound with electronic specific heat coefficient γ = 95 mJ/mol K2 and Pauli paramagnetic susceptibility χ0 0.0115 emu/mol. The density of states of single crystal YbPd2Si2 is approximately half that of polycrystalline YbPd2Si2 while the strength of the Kondo effect in the single crystal is approximately twice that of poly crystal
We report the synthesis of three new Yb-based equiatomic compounds YbPdZn, YbPtZn, and YbAuZn, and o...
The crystal field excitations of the rare earth intermetallic compound YbMn2Si2 have been measured b...
High quality single crystals of LaCu2Si2 are successfully grown from a high temperature ternary melt...
Single crystals of YbPt2Si2 and Yb2Pt3Si5 have been prepared by solvent growth method with Sn flux, ...
Heat capacity of YbPd2Si2 has been measured in the temperature range 1.5 to 20 K. The coefficient of...
We report on the single crystal growth of the heavy-fermion compounds YbRh2Si2 and YbIr2Si2 using a ...
We report on synthesis, crystal structure, magnetic, thermodynamic, and transport properties of the ...
We report the first thorough characterization of single crystals of CeCu2Si2. Measurements on these ...
From heat capacity and magnetic susceptibility results, we conclude that YbPt2Si2 is a homogeneously...
A new compound NpPd2Sn was prepared and studied by means of X-ray diffraction, magnetization, electr...
The superconducting and magnetic properties of YNi(2)B(2)C single crystal have been investigated by ...
We consider the local properties of the Yb3+ ion in the crystal electric field in the Kondo lattice ...
Single-crystals of the heavy-electron compound U2Pt2In have been grown aby a modified mineralization...
YbNiSb has a cubic MgAgAs-type structure and the Yb ions are trivalent. The heat capacity, C, measur...
Single crystals of CeM2 and GdM2 (M = Ag, Al, and Si) were grown by the flux growth technique and ch...
We report the synthesis of three new Yb-based equiatomic compounds YbPdZn, YbPtZn, and YbAuZn, and o...
The crystal field excitations of the rare earth intermetallic compound YbMn2Si2 have been measured b...
High quality single crystals of LaCu2Si2 are successfully grown from a high temperature ternary melt...
Single crystals of YbPt2Si2 and Yb2Pt3Si5 have been prepared by solvent growth method with Sn flux, ...
Heat capacity of YbPd2Si2 has been measured in the temperature range 1.5 to 20 K. The coefficient of...
We report on the single crystal growth of the heavy-fermion compounds YbRh2Si2 and YbIr2Si2 using a ...
We report on synthesis, crystal structure, magnetic, thermodynamic, and transport properties of the ...
We report the first thorough characterization of single crystals of CeCu2Si2. Measurements on these ...
From heat capacity and magnetic susceptibility results, we conclude that YbPt2Si2 is a homogeneously...
A new compound NpPd2Sn was prepared and studied by means of X-ray diffraction, magnetization, electr...
The superconducting and magnetic properties of YNi(2)B(2)C single crystal have been investigated by ...
We consider the local properties of the Yb3+ ion in the crystal electric field in the Kondo lattice ...
Single-crystals of the heavy-electron compound U2Pt2In have been grown aby a modified mineralization...
YbNiSb has a cubic MgAgAs-type structure and the Yb ions are trivalent. The heat capacity, C, measur...
Single crystals of CeM2 and GdM2 (M = Ag, Al, and Si) were grown by the flux growth technique and ch...
We report the synthesis of three new Yb-based equiatomic compounds YbPdZn, YbPtZn, and YbAuZn, and o...
The crystal field excitations of the rare earth intermetallic compound YbMn2Si2 have been measured b...
High quality single crystals of LaCu2Si2 are successfully grown from a high temperature ternary melt...