These spectra compare the Ti 2p core-level XPS line shape for atomically clean, stoichiometric samples of Ti, Ti2O3, and TiO2; the latter two are UHV-cleaved or fractured single crystals. The Ti0 and Ti4+ peaks of Ti metal and TiO2, respectively, exhibit the simple shapes expected for such core levels. The Ti3+ peaks of Ti2O3, however, are more complex, although there are no other valence states of Ti in the sample
Satellites in core level spectra of photoelectron spectroscopy (PES) can provide crucial information...
<p><b>Table 3.</b> Error budget for the peak energy of all the spectral profiles of Ti Kβ that go in...
The EDS elemental analysis of (a) Ti-NT and (b) Ti-6Al-4V-NT showing presence of only Ti and O in Ti...
Ti2O3 is a semiconducting transition-metal oxide with a 0.1 eV bandgap at room temperature and is th...
<p>XPS spectra of (a) Au/N-TiO<sub>2</sub> and core level spectra of (b) O 1s, (c) N 1s, and (d) Au ...
A bstract The determination of the oxidation state and structural role of transition metals in min...
There is almost a factor of 2 increase in the full width at half maximum (FWHM) of the main Ti 2p<su...
The present work was devoted to the X-ray photoelectron spectroscopy (XPS) investigation of the prin...
<p>The XPS high-resolution spectra of Ti 2p and O 1s for bare Ti (a), Ti 2p and N 1s for TiN-coated ...
<p><strong>Figure 5.</strong> Typical fit of a Ti Kβ spectrum. The crystal clinometer voltage was −1...
The determination of the oxidation state and structural role of transition metals in minerals, espec...
Using a configuration-interaction impurity-Anderson model we calculate core-hole X-ray Photoemission...
<p><strong>Figure 6.</strong> The peak energies of the fits of individual measured Ti Kβ spectra. Ea...
MXenes are an interesting family of 2D materials that have the potential to meet challenges in many ...
<p>A) The XPS survey spectra obtained for the BASE(red) and RAPID (blue) implants as received. On bo...
Satellites in core level spectra of photoelectron spectroscopy (PES) can provide crucial information...
<p><b>Table 3.</b> Error budget for the peak energy of all the spectral profiles of Ti Kβ that go in...
The EDS elemental analysis of (a) Ti-NT and (b) Ti-6Al-4V-NT showing presence of only Ti and O in Ti...
Ti2O3 is a semiconducting transition-metal oxide with a 0.1 eV bandgap at room temperature and is th...
<p>XPS spectra of (a) Au/N-TiO<sub>2</sub> and core level spectra of (b) O 1s, (c) N 1s, and (d) Au ...
A bstract The determination of the oxidation state and structural role of transition metals in min...
There is almost a factor of 2 increase in the full width at half maximum (FWHM) of the main Ti 2p<su...
The present work was devoted to the X-ray photoelectron spectroscopy (XPS) investigation of the prin...
<p>The XPS high-resolution spectra of Ti 2p and O 1s for bare Ti (a), Ti 2p and N 1s for TiN-coated ...
<p><strong>Figure 5.</strong> Typical fit of a Ti Kβ spectrum. The crystal clinometer voltage was −1...
The determination of the oxidation state and structural role of transition metals in minerals, espec...
Using a configuration-interaction impurity-Anderson model we calculate core-hole X-ray Photoemission...
<p><strong>Figure 6.</strong> The peak energies of the fits of individual measured Ti Kβ spectra. Ea...
MXenes are an interesting family of 2D materials that have the potential to meet challenges in many ...
<p>A) The XPS survey spectra obtained for the BASE(red) and RAPID (blue) implants as received. On bo...
Satellites in core level spectra of photoelectron spectroscopy (PES) can provide crucial information...
<p><b>Table 3.</b> Error budget for the peak energy of all the spectral profiles of Ti Kβ that go in...
The EDS elemental analysis of (a) Ti-NT and (b) Ti-6Al-4V-NT showing presence of only Ti and O in Ti...