Bending failure analysis and modeling of thin fiber reinforced shells
- Pappas, Georgios A.
- Schlothauer, Arthur
- Ermanni, Paolo
DOIAbstract
In this work, the impact of high stress gradients, found in bending of thin unidirectional fiber reinforced shells (~0.1 to 1 mm), on compressive micro-buckling failure, was analyzed. Such thin shells show increased resistance to compressive failure under high curvatures, which may even allow tensile fiber damage to drive ultimate failure for very low thickness (e.g. <0.5 mm). The main scope of this work is to analyze this increased resistance to compressive failure and propose a robust modeling scheme. The mechanical failure response was captured by a shell-buckling experimental campaign. The origins of the increased compressive failure resistance were initially attributed to the reduction of shear stresses acting on the most susceptible d...