PENGARUH KOMPOSISI BLENDING DAN NON PELARUT TERHADAP KINERJAMEMBRAN Polyvinylidene fluoride(PVDF) - KITOSAN DALAM PEMISAHAN PEWARNARHODAMIN-BINFLUENCE OF BLENDING AND NON-SOLVENT H2O/C2H5OH COMPOSITION TOPolyvinylidene fluoride(PVDF)–CHITOSAN MEMRANE PRFORMANCE IN THESEPARATION OF RHODAMIN-B

Abstrak. Telah dilakukan penelitian tentang pembuatan membran Polyvinylidene fluoride (PVDF) blending kitosanserta pemanfaatannya pada pemisahan limbah pewarna rhodamin B. Pada penelitian ini dilakukan variasi komposisiblending kitosan dan komposisi non pelarut yang bertujuan untuk mengetahui pengaruh komposisi blending kitosandan non pelarut terhadap kekuatan mekanik, fluks, dan rejeksi serta uji morfologi permukaan pada membran terbaik.Pembuatan membran pada penelitian ini menggunakan metode preparasi inversi fasa dengan teknik perendapanpengendapan.Membran PVDF-kitosan padat kemudian diuji kekuatan mekanik pada membran menggunakan alatautograph. Fluks menggunakan alat dead end dan rejeksi menggunakan alat spektrofotometer UV-Vis. Hasil yangdiperoleh pada penelitian ini yaitu membran pada komposisi 16/0/84/0 (PVDF/kitosan/NMP/NH4Cl) dengan nonpelarut 50% air/50% etanol memiliki nilai modulus young terbesar sebesar 2248 N/m2. Membran pada komposisi16/0/84/0 PVDF/kitosan/NMP/NH4Cl) dengan non pelarut 75% air/25% etanol memiliki nilai fluks terbesar sebesar2112 Lm-2jam-1 dan nilai koefisien rejeksi terbesar sebesar 96,24 %. Berdasarkan hasil penelitian yang diperoleh,dapat disimpulkan bahwa komposisi blending dan non pelarut berpengaruh terhadap karakteristik mekanik dan kinerjamembran. Semakin banyak komposisi PVDF dalam larutan cetak dan semakin banyak presentase non pelarut etanolmaka semakin besar nilai modulus young, semakin kecil nilai fluks dan semakin besar nilai rejeksi yang dihasilkan.Berdasarkan nilai modulus young dan fluks membran, diperoleh membran PVDF-kitosan dengan komposisi terbaikyaitu pada komposisi 13/1,5/84/1,5 (PVDF/kitosan/NMP/NH4Cl) dengan non pelarut 75% air/25% etanol. Hasil dariuji morfologi membran yang terbaik melalui SEM dengan perbesaran 5000x, membran memiliki struktur pori yangrapat serta memiliki pori dengan ukuran pori 0,001695 μm.Kata kunci: membran PVDF-Kitosan,kinerja, karakteristik mekanik, pewarna rhodamin B, pengolahan limbahAbstract. A research had been done on the preparation of polyvinylidene fluoride (PVDF) membrane blendingchitosan and its utilization in waste separation of rhodamine B as a dye. This research is done by variating chitosanblending composition and non-solvent composition which aimed to determine the effect of chitosan blendingcomposition and non-solvent to mechanical strength, flux, and rejection as well as the morphology test of the bestmembrane. The preparation of membranes was using the phase inversion method with immersion-precipitationtechnique. Solid PVDF-chitosan membranes was determined its mechanical strength by using autograph. Flux of themembranes was determined by using a dead-end and its rejection by using spektrophotometer UV-Vis. The results ofthis research showed that the membrane of composition 16/0/84/0 (PVDF/chitosan/NMP/NH4Cl) with non solvent 50%of water/50% of ethanol has maximum modulus young value 2248 N/m2. Based on the results obtained, it can beconcluded that the composition of the blending and non-solvent effect on the mechanical characteristics and theperformance of the membrane. The more the composition of PVDF in solution the print and the more percentage thenon solvent ethanol, then the greater the value of modulus young, the smaller value of the flux and the greater theresulting rejection value. Membrane of composition 16/0/84/0 (PVDF/chitosan/NMP/NH4Cl) with non solvent 75% ofwater/25% of ethanol has maximum flux value 2112 Lm-2hour-1 and maximum rejection coefficient on 96,24%. Basedon modulus young and flux value of membrane, showed that the best PVDF-chitosan membrane was on composition13/1,5/84/1,5 (PVDF/chitosan/NMP/NH4Cl) ) with non solvent 75% of water/25% of ethanol. The results of the test thebest membrane morphologhy through SEM with a magnification of 5000x membrane porous structure, dense andhas a pore with a pore size 0,001695 μm.Keywords: membranes, PVDF-Chitosan, waste handlin