Komparativno istraživanje korozije žice korištene pri urološkoj obradi uz sterilizaciju

The purpose of the tests was to determine whether and how sterilization process of samples made of AISI 316L stainless steel with different strain impacts their corrosion resistance. Tests were made on steel samples that had been electrochemically polished in order to assure proper surface roughness. In order to evaluate the influence of sterilization on physical and chemical properties of steel surface, tests of corrosion resistance were made by means of potentiodynamical method. The tests were made in alternative solution simulating human urine. Recorded anodic polarization curves created the ground for determination of typical parameters describing pitting corrosion resistance, that enabled to evaluate steel wire corrosion behavior under sterilization conditions.Svrha je ispitivanja bila da se ustanovi postoji li, i kakav je utjecaj sterilizacije na korozijsku otpornost žičanih uzoraka od nehrđajućeg čelika AISI 316L, oblikovanih plastičnom deformacijom različitog intenziteta. Ispitivanja su obavljena na uzorcima koji su elektrokemijski polirani kako bi se osigurala tražena niska hrapavost površine. U cilju procjene utjecaja sterilizacije na fizikalna i kemijska svojstva čelične površine, ispitivana je korozijska otpornost potenciodinamičkom metodom. Pritom je za simulaciju ljudske mokraće primijenjena zamjenska otopina. Snimljene krivulje anode polarizacije poslužile su za određivanje tipičnih parametara koji definiraju otpornost čelika prema jamičastoj koroziji, što je omogućilo procjenu korozijskog ponašanja čeličnih žica nakon sterilizacije