Influence of Polymerization Light Intensity on the Polymerization Shrinkage of Composite Materials (Part III)

Kompozitni materijali skupljaju se tijekom procesa polimerizacije što umanjuje njihovu kliničku vrijednost. Modifikacija u sastavu kompozitnoga materijala i tehnika aplikacije kompozita pokazale su se nedostatnima za kompenzaciju polimerizacijskoga skupljanja, pa se je zato pokušalo s modifikacijom polimerizacijskih programa. Polimerizacijski programi nižega intenziteta omogućit će dužu pregelacijsku fazu i time uvelike smanjiti ukupan iznos skupljanja. Svrha rada bila je odrediti polimerizacijsko skupljanje Tetric Ceram (Vivadent, Schaan, Liechtenstein) i Filtek Z 250 (3M Dental Products, St. Paul, MN) kompozitnoga materijala postupkom digitalne holografske interferometrije. Uzorci kompozitnih materijala polimerizirani su trima programima različita intenziteta (srednji, eksponencijski i standardni) Elipar Trilight halogene žarulje (ESPE, Seefeld, Germany). Najviše vrijednosti polimerizacijskoga skupljanja zabilježene su kod polimerizacijskoga programa s najjačim intenzitetom svjetla.Composite materials shrink during the polymerization process which lessens their clinical value. Modifications of composition of the composite material and application technique proved inadequate for compensation of polymerization shrinkage, and therefore modification of polymerization modes was attempted. The polymerization modes of lower intensities will enable prolongation of the pre-gelation phase and consequently greatly decrease the total amount of shrinkage. The purpose of the study was to determine the polymerization shrinkage of Tetric Ceram (Vivadent, Schaan, Liechtenstein) and Filtek Z 250 (3M/ESPE Dental Products, St Paul, MN) composite materials by digital holographic interpherometry. Samples of the composite material were polymerized by three modes of various intensities (medium, exponential and standard) Elipar Trilight halogen curing unit (3M/ESPE, Seefeld, Germany). Highest values of the polymerization shrinkage were recorded for the polymerization mode with highest light intensity