The Relationship between Coating Property and Solid Particle Erosion Resistance of AIP-Deposited TiAlN Coatings with Different Al Contents

TiAlN coatings with different Al ratios were deposited by the cathodic arc ion plating (AIP) method, and the relationship between solid particle erosion resistance and structural, mechanical properties was investigated by a micro slurry-jet erosion (MSE) test. The crystal structure of TiAlN coating changes depending on the Al ratio. The coating shows a B1 single cubic phase between the Al ratio of 0 and 0.58; above this ratio, formation of a B4 hexagonal phase is observed. The mechanical properties such as hardness and Young’s modulus of the TiAlN coating also depend on the Al ratio and the crystal structure. The erosion rate decreases by increasing the Al ratio up to 0.58, as the coating is a cubic single phase. The TiAlN coating shows the lowest erosion rate at an Al ratio of 0.58. The erosion rate increases drastically as the crystalline phase changes from the B1 cubic to B4 hexagonal phase at the Al ratio of more than 0.58. The change in erosion rate is also discussed in connection with mechanical properties such as erodent particle hardness to coating hardness ratio and coating hardness to Young’s modulus ratio