Bond strength evaluation of the veneering-core ceramics bonds

The purpose of this study was to determine whether the bond of veneering porcelain to a ceramic core in bilayered ceramics was similar to that of the metal ceramic control of well known behaviour. Six groups of nine specimens each were fabricated, whose dimensions were 15 mm long and 8 mm in diameter at the core, and 2 mm long and 8 mm in diameter for the veneer. The groups were GR. 1 (control group): CrNi alloy/d.SIGN (Ivoclar), GR. 2: IPS e.maxPress/IPS e.maxCeram (Ivoclar), GR. 3: IPS e.maxZirCad/ IPS e.maxZirPress (Ivoclar), GR. 4: IPS e.maxZirCad/IPS e.maxCeram (Ivoclar), GR. 5: Lava Frame (3M ESPE)/ Lava Ceram (3M ESPE) and GR. 6: Lava Frame (3M ESPE)/IPS e.maxCeram (Ivoclar). A shear strength test was used in all samples with a universal testing machine. The chosen crosshead speed was of 0.50 mm/min. The obtained results were analyzed using a one way analysis of variance test (ANOVA) to determine whether significant differences existed between the groups whether significant differences existed between the groups (p