Rapid Secondary Recrystallization of the Goss Texture in Fe₈₁Ga₁₉ Sheets Using Nanosized NbC Particles

Herein, a simple and efficient method is proposed for fabricating Fe81Ga19 alloy thin sheets with a high magnetostriction coefficient. Sharp Goss texture ({110}) was successfully produced in the sheets by rapid secondary recrystallization induced by nanosized NbC particles at low temperatures. Numerous NbC precipitates (size ~90 nm) were obtained after hot rolling, intermediate annealing, and primary recrystallization annealing. The relatively higher quantity of nanosized NbC precipitates with 0.22 mol% resulted in finer and uniform grains (~10 μm) through thickness after primary recrystallization annealing. There was a slow coarsening of the NbC precipitates, from 104 nm to 130 nm, as the temperature rose from 850 °C to 900 °C in a pure nitrogen atmosphere, as well as a primary recrystallization textured by strong γ fibers with a peak at {111} favoring the development of secondary recrystallization of Goss texture at a temperature of 850 °C. Matching of the appropriate inhibitor characteristics and primary recrystallization texture guaranteed rapid secondary recrystallization at temperatures lower than 950 °C. A high magnetostriction coefficient of 304 ppm was achieved for the Fe81Ga19 sheet after rapid secondary recrystallization