Influence of aging on bond strength of artificial teeth to denture base acrylic resins

Aim: The aim of this study was to evaluate the bond strength of artificial teeth to different types of denture base resins when submitted to thermomechanical cycling (TMC). Methods: Sixty artificial mandibular first molars (Trilux, Vipi) were randomly divided into 3 groups according to denture base acrylic resins (Vipi Wave, Vipi Cril, and Vipi Cril Plus, Vipi). The teeth were fixed onto self-polymerizing acrylic resin bars (0.5 cm2 cross-section x 2 cm height), and the set was included in a metal flask using dental stone/silicone. After the dental stone was set, the bar was removed, and the denture base resin was packed and processed according to the group studied (Vipi Wave: 180 W/20 minutes + 540W/5 minutes; Vipi Cril and Vipi Cril Plus: Water bath at 74ºC for 9h). After polymerization, the samples were divided into 2 groups (n=10), according to the TMC treatment received (simulation of 5 years of mastication or not). The samples were submitted to tensile bond strength test (1 mm/min), and the data (MPa) were statistically analyzed (2-way ANOVA, Bonferroni, α=0.05). The fracture interfaces were evaluated using a stereomicroscope (50x). Results: The bond strength results showed no statistically significant difference (p>0.05) between the resins studied. TMC was significant (p