Investigation of 9000 hours multi-stress aging effects on High-Temperature Vulcanized Silicone Rubber with silica (nano/micro) filler hybrid composite insulator

Degradation in the polymeric insulators is caused due to the environmental stresses. The main aim of this paper is to explore the improved aging characteristics of hybrid samples by adding nano/micro silica in High Temperature Vulcanized Silicone Rubber (HTV-SiR) under long term accelerated aging conditions for 9000 hours. As HTV-SiR is unable to sustain environmental stresses for a long time, thus a long term accelerated aging behavior is an important phenomenon to be considered for field application. The aging characteristics of nano/micro filled HTV-SiR are analyzed by using techniques such as Scanning Electron Microscopy (SEM), Leakage Current (LC), Fourier Transform Infrared Microscopy (FTIR), Hydrophobicity Classification (HC), and breakdown strength for the aging time of 9000 hours. FTIR and leakage currents are measured after every cycle. All the co-filled samples revealed escalated aging characteristics as compared to the neat sample except the SN8 sample (8% nano-silica+20% micro-silica) after 9000 hours of aging. The highest loading of 6% and 8% nano-silica with 20% micro-silica do not contribute to the improved performance when compared with the neat and hybrid samples. However, from the critical experimental analysis, it is deduced that SN2 sample (2% nano-silica+20% micro-silica) is highly resistant to the long term accelerated aging conditions. SN2 has no cracks, lower loss percentages in the important FTIR absorption peaks, higher breakdown strength and superior HC after aging as compared to the unfilled and hybrid samples