An XRD Study of Chemical Self-Discharge in Delithiated Cobalt Oxide

International audienceChanges in samples of Li1–xCoO2 were measured by X-ray diffractometry (XRD) after thermal aging treatments that cause capacity losses in electrochemical cells. Changes in lattice parameters were used to identify lithium re-intercalation into Li1–xCoO2 when it was aged in the presence of LiClO4, LiPF6, and LiAsF6 in propylene carbonate (PC). Li+ re-intercalation could account for the reversible capacity loss. Thermal aging at 75°C in pure PC or pure argon gas resulted in other changes that are attributed to the formation of spinel phase. The rate of the lithium re-intercalation increases in the following sequence: LiPF64