Технологічна міцність аустенітних сталей та сплавів в навколосолідусному інтервалі температур

The analysis of existent looks is conducted to character of change of mechanical properties of metal of the weld during his primary crystallization from a liquid phase. Structural and technological factors are considered influencing on resistance of high-alloy steels and Ni-alloys against formation of liquation cracks at welding. It is indicated on the necessity of generalization of existent presentations and their addition with bringing in of modern physical models of mechanics of high temperature brittleness. The analysis of existent looks is conducted to character of change of mechanical properties of metal of the weld during his primary crystallization from a liquid phase. Structural and technological factors are considered influencing on resistance of high-alloy steels and Ni-alloys against formation of liquation cracks at welding. It is indicated on the necessity of generalization of existent presentations and their addition with bringing in of modern physical models of mechanics of high temperature brittleness.Проведен анализ существующих взглядов на характер изменения механических свойств металла сварного шва во время его первичной кристаллизации из жидкой фазы. Рассмотрены структурные и технологические факторы влияющие на стойкость высоколегированных сталей и сплавов никеля против образования кристаллизационных горячих трещин при сварке. Указано на необходимость обобщения существующих представлений и их дополнения с привлечением современных физических моделей механики высокотемпературного хрупкого разрушения двухфазного твердо-жидкого тела