Phase transformations and surface characterization of the platinumchromium coated system

This research involves the investigation of phase transformations in the platinum-chromium coated system. Single-layer 0.1μm platinum coatings were deposited via electron beam deposition on 99.98 percent pure chromium substrates. Specimens were subjected to systematic heat treatment in a vacuum furnace at 900°C for up to 20 hours. Phase formation and the changes in surface morphology were investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM). Both CrPt and Cr3Pt phases are formed during heat treatment for different times at 900°C. Significant changes in the morphology of this coated system were detected after heat treatment at 900°C for 20 hours.4 page(s