Analysis of penetration of experimental resin materials into initial enamel caries by CLSM

O objetivo deste trabalho foi avaliar a penetração de materiais resinosos experimentais de baixa viscosidade em lesões artificiais sub-superficiais de cárie em esmalte (LASCE), por meio de Microscopia Confocal de Varredura a Laser (MCVL). Cinquenta e cinco terceiros molares humanos extraídos e livres de cárie foram selecionados. Blocos da superfície oclusal foram obtidos e distribuídos em 11 grupos (n=5), dos quais 5 blocos foram mantidos hígidos (Grupo Controle Positivo) e os demais submetidos a produção de cárie in vitro. Os blocos de esmalte oclusal cariados foram distribuídos aleatoriamente de acordo com a composição do material em: Grupo Controle Negativo (dente cariado); G1: 100% TEGDMA, G2: 80% TEGDMA + 20% etanol, G3: 80% TEGDMA + 20% HEMA, G4: 75% TEGDMA + 25% UDMA, G5: 60% TEGDMA + 20% UDMA + 20% etanol, G6: 60% TEGDMA + 20% UDMA + 20% HEMA, G7: 75% TEGDMA + 25% BisEMA, G8: 60% TEGDMA + 20% BisEMA + 20% etanol e G9: 60% TEGDMA + 20% BisEMA + 20% HEMA. Os materiais experimentais foram impregnados com corante isotiocianato de rodamina B a 0,1 % anterior a aplicação na superfície oclusal, e após fotoativado (40 s), os blocos foram seccionados em fatias de 0,5 mm, e estas foram deixadas em solução etanólica de fluoresceína de sódio 100 ?M por 3 min, para visualização em Microscopia Confocal de Varredura a Laser. A análise das imagens foi feita através do programa LAS AF Lite, e em seguida as médias de intensidade foram convertidas em porcentagem pelo Microsoft Excel. Os valores de porcentagem obtidos foram submetidos a análise de variância e teste de Tukey, em nível de significância de 5%. Os resultados mostraram que a maior média de intensidade de fluorescência, indicando o maior percentual de preenchimento ocorrido na lesão de cárie, ocorreu no G7, enquanto o menor valor foi obtido pelo grupo G5. Pode-se concluir que diferentes concentrações monoméricas e composição de misturas em composto resinoso de baixa viscosidade produzem diferentes percentuais de penetração e preenchimento de lesões cariosas em esmalte. Os maiores valores de preenchimento das lesões foram obtidos com a mistura TEGDMA+BisEMA e os mais baixos para TEGDMA+UDMA+etanol.The aim of this study was to evaluate the penetration of low viscosity experimental resin materials containing different combinations of resin monomers/diluents in enamel-like caries lesions using Confocal Laser Scanning Microscopy (CLSM). Nine experimental resin materials containing TEGDMA as a base monomer and varying the other monomers and solvents BisEMA, HEMA, UDMA and ethanol were prepared in different proportions. Fifty and five sound and extracted third human molars were used. The crown fragments were obtained and distributed in 11 groups (n=5), which 5 crown fragments were maintained sound (Positive Control Group) and the others were submitted to in vitro lesion caries production. The crown fragments were distributed randomly according to material composition: Negative Control Group (carious teeth); Carious and infiltrated blocks: G1: 100% TEGDMA, G2: 80% TEGDMA + 20% ethanol, G3: 80% TEGDMA + 20% HEMA, G4: 75% TEGDMA + 25% UDMA, G5: 60% TEGDMA + 20% UDMA + 20% ethanol, G6: 60% TEGDMA + 20% UDMA + 20% HEMA, G7: 75% TEGDMA + 25% BisEMA, G8: 60% TEGDMA + 20% BisEMA + 20% ethanol and Group 9: 60% TEGDMA + 20% BisEMA + 20% HEMA. Experimental materials were labeled with the red fluorophore rhodamine B isothiocyanate (RITC 0,1%; Sigma Aldrich, Steinheim, Germany) prior to the application on occlusal surface, and after light cured (40 s), 0,5 mm thin sections were prepared and immersed in a 50% ethanolic solution of 100 ?M sodium fluorescein (NaFL, Sigma Aldrich) for 3 min, to confocal microscopy visualization. Analysis of images was made by program LAS AF Lite, then, intensity means were converted in percentage by Microsoft Excel. Percentage values obtained were submitted to ANOVA Tukey's test, at significance level of 5%. Results showed that that the highest mean of fluorescence intensity, indicating fulfilling percentage penetration occurred into caries lesion, was obtained in the G7, while lower value was obtained by G5. It could be concluded that different monomeric concentrations and composition of low viscosity resin blends produce different percentage of penetration and fulfilling of initial enamel-like caries lesions. The best results were obtained for TEGDMA+BisEMA and the lowest results for TEGDMA+UDMA+ethanol