Thermal and structural investigation of Er:YAl(3)(BO(3))(4) nanocrystalline powders

Pure Er:YAB (Er:YAl(3)(BO(3))(4)) nanometer-sized crystalline powder was produced from low cost chemical route, the polymeric precursor method. The initial homogeneous solutions were heat treated from 200 to 700A degrees C under oxygen atmosphere and the unique crystalline phase was synthesized at around 1150A degrees C. The thermal treatments and the initial stoichiometry play a very important role on the Er:YAB preparation. The thermal events of amorphous precursor resins and the crystallization process up to phase formation were investigated