Solid-Liquid Phase Diagram of the Binary System Octadecanoic Acid and Octadecanol and the Thermal Chemical Property of the Composition at Eutectic Point

Phase diagram is a powerful tool to guide the exploitation of thermal energy materials. Heat storage technology of phase-change material (PCM) was widely used to solve major energy utilization problems on large energy consumption and low utilization efficiency. In this work, a novel solid-liquid phase diagram of the binary system octadecanoic acid (C18-acid) + octadecanol (C18-OH) was investigated using the differential scanning calorimeter (DSC). The phase-change temperature and phase-change enthalpies against the composition of C18-acid and C18-OH were determined experimentally, and then the binary phase diagram of T–X (X expresses the mass fraction of C18-OH in the two components of C18-acid and C18-OH) was established for the first time. The phase diagram belongs to a binary simple system with one eutectic point, and the content of C18-OH at eutectic point is 0.4 in mass fraction. Neither solid solution nor copolymer was formed. The thermal chemical properties on the phase-change latent heat (Q), phase-change temperature (Tp), and the thermal conductivity (λ) for the composition at the eutectic point of the binary system are 198.7 J·g−1, 44.2°C, and 0.2352 W·m−1·K−1, respectively. This result indicates that the material at eutectic point has a great potential to be used as energy storage material for supply of heat and scouring bath