Electrochemical properties of manganese ferrite-based supercapacitors in aqueous electrolyte: the effect of ionic radius

The electrochemical performances of symmetric supercapacitors assembled by MnFeO colloidal nanocrystal clusters (CNCs) in aqueous electrolytes were investigated by using cyclic voltammetry, galvanostatic charge-discharge, cycle stability and electrochemical impedance spectroscopy. Results showed that the capacitance of MnFeO CNCs can be easily adjusted by the controlled electrolytes. It was found that the specific capacitances of CNCs-based electrodes were 97.1, 93.9, 74.2 and 47.4Fg for the electrolytes (2M) containing KOH, NaOH, LiOH and NaSO, respectively, at the current density of 0.1Ag. The capacitance of the electrode was increased from 56.9 to 152.5Fg with aqueous KOH electrolytes changed from 0.5M to 6M. The MnFeO CNCs-based supercapacitor using aqueous KOH (6M) electrolyte displayed the best cycle stability among all the supercapacitors. Based on the experimental results, the enhancement mechanism of electrochemical performances for the CNCs-based supercapacitors was proposed