The changes in the structure and chemical composition of dental enamel as a result of application of exogenous methods for preventing dental caries in children with disabilities

Scopul lucrării a constituit studiul modificărilor de structură şi a compoziţiei chimice a smalţului dentar survenite în urma aplicării metodelor exogene de prevenire a cariei dentare la copiii cu dizabilităti severe. 7 Material şi metode: în studiu au fost luaţi 144 copii cu dizabilitâţi severe, având vârsta cuprinsă între 13 şi 15 ani. înfucţie de măsurille cariopreventive aplicate, copiii au fost divizaţi în 3 loturi: Lt a inclus 48 copii care au beneficiat defluorizare profundă a smalţului dentar; în L 1 s-a aplicat metoda fizico-chimică de prevenire a cariei dentare (laseroterapie şi fluorizare profundă a smalţului), lotul de control (LJ a inclus 52 copii la care s-a realizat periajul dentar cu paste fluorurate. Pentru cercetarea structurii şi compoziţiei chimice a smalţului dentar, 24 de dinţi extraşi în scop ortodontic au fost studiaţi prin microscopie electronică cu baleiaj-SEM şi li s-a efectuat microanaliză radio-spectrală prin metoda spectroscopiei radiografice energodispersânte. Ca urmare a aplicării metodelor exogene de prevenire a cariei dentare, în loturile L/ şi L, la suprafaţa şi în straturile profunde ale smalţului s-a depistat depozitarea micro-globulelor de CaF1 MgF, şi CuFv reducerea considerabilă a concentraţiei carbonului, normalizarea relaţiei Ca/P şi majorarea semnificativă a conţinutului fiuorului. Metoda fizico-chimică de prevenire a contribuit la majorarea concentraţiei F de 1,63 ori în straturile superficiale şi de 2,08 ori în straturile profunde ale smalţului, asigurând astfel un efect cariopreventiv sporit, comparativ cu metoda de fluorizare profundă a smalţului. Concluzie: aplicarea simultană a laseroterapiei cu nanofluoruri la copiii cu dizabi/ităţi severe asigură un efect carioprotector maxim. The purpose of this work was to study the changes in the structure and chemical composition of dental enamel occurred as a result of application of exogenous methods for preventing dental caries in children with severe disabilities. Material and methods: 144 children with severe disabilities have been involved in the study, aged between 13 and 15 years. Depending on the caries preventive measures applied, the children were divided into 3 groups: L/ included 48 children who benefited from profound fluoridation of dental enamel; in L, the physicochemical method was applied to prevent dental caries (laser therapy and pro found dental enamel fluoridation); the control group (LJ included 52 children that underwent tooth brushing with fluoride toothpaste. In order to investigate the structure and chemical composition of dental enamel of 24 teeth extracted following orthodontic indications the scanning electron microscopy SEM, and radio spectral microanalysis was performed by the energy-dispersant radiographic spectroscopy method. As a result of application of exogenous methods for preventing dental caries in groups L/ and L, on the surface and in deeper layers of enamel we found deposits of CaF, MgF 1 and CuF 1 micro-globules, considerable reduction of carbon concentration, normalization of Ca/P ratio, and significant increase of fluorine content. The physicochemical prevention method helped increase 1.63 times the F concentration in the surface layers of enamel and respectively 2.08 times in the adamantine depth, ensuring a greater caries preventive effect compared with profound fluoridation of dental enamel. Conclusion: the simultaneous application of laser therapy and in children with severe disabilities offers a maximum protective effect