Thermo-mechanical Characterization of an Aged Ni45.3Ti39.7Hf10Pd5 Shape Memory Alloy

© 2020, The Minerals, Metals & Materials Society.Thermo-mechanical characterization of a Ni45.3Ti39.7Hf10Pd5 polycrystalline shape memory alloy after aging at 550°C for 3 h was conducted. Thermal cycling under constant stress,superelasticity and loading till failure tests were employed to reveal the shape memory and material properties. Recoverable shape memory strain of 3.8% was achieved under compressive stress of 500 MPa. The sample showed almost perfect superelasticity above 70°C with total recoverable strain of about 4%, but failed at 2340 MPa with compressive strain > 13% at 35°C, and aging was not found to significantly affect its shape memory behavior because of the low volume fraction of precipitates