Examination of the influence of coatings on thin superalloy sections. Volume 1: Description and analysis

The effects of an aluminide coating and of section thickness were investigated on two cast nickel-base superalloys. Cast section thickness ranged from 0.038 cm to 0.15 cm. Simulated engine exposures in a jet fuel burner rig with cyclic air cooling were studied. The effects of surface machining before coating and re-machining and re-coating after exposures were examined. The properties evaluated included tensile strength, stress rupture, high-cycle mechanical fatigue, and thermal fatigue. A metallurgical analysis was made of the microstructures of the coated and uncoated alloy